The Utilization of Platinum Catalysts Deposited on Carbon Support Synthesized From Coffee Grounds in a Polymer Electrolyte Membrane Fuel Cell
ISEF · 2023 Chemistry
Overview
Hydrogen is a clean energy source with tremendous unrealized potential. When oxidated in a polymer electrolyte membrane fuel cell (PEMFC), it produces energy at a rapid rate, whilst only producing water as a byproduct. However, widespread use of PEMFCs is limited by the expensive components required, such as catalysts. As the properties of the catalyst material are largely determined by the support on which it is deposited, this project aims to synthesize an electrochemically active catalyst material, deposited onto carbon derived from coffee grounds. Carbon material was synthesized using zinc chloride activated pyrolysis and the Pt nanoparticles were deposited on coffee carbon (Pt(CGDC)) and commercial carbon (Pt(KB)) using two methods: using ethylene glycol or hydrogen as a reducing agent. Thermogravimetric analysis displayed that catalyst materials contained roughly 60 wt% of Pt, nitrogen sorption analysis showed that all studied materials were micro-mesoporous, X-ray diffraction revealed Pt crystallite size was found to be in correlation with catalytic properties and high-resolution scanning electron microscopy determined that the average Pt particle size is 4.7±2.5 nm. PEMFC measurements revealed that Pt(CGDC) produced comparable electrochemical activity to Pt(KB). Specifically, Pt(CGDC) produced a higher electrochemically active surface area of 64 m(Pt)^2/g(Pt), compared to Pt(KB) with a value of 51 m(Pt)^2/g(Pt). Despite that, both catalyst materials produced similar current densities at 670 mV of 0.68 A/cm^2 (Pt(CGDC)) and 0.70 A/cm^2 (Pt(KB)). In addition, both produced comparable maximum power density of 0.56 W/cm^2 and W/cm^2 respectively.
Competition history
- ISEF 2023
Resources
Related projects
ISEF · 2017
Economical Oxygen Reduction Electrocatalysts: Alternatives to Platinum for Proton Exchange Membrane Fuel Cells
ISEF · 2019
Application of Electrospun Poly(acrylic acid)-Platinum/Carbon Catalyst Ink to Optimize Polymer Electrolyte Membrane Fuel Cell Performance
ISEF · 2016
Incorporation of Platinum and Gold Partially Reduced Graphene Oxide into Polymer Electrolyte Membrane Fuel Cells for Increased Output Power and Carbon Monoxide Tolerance
ISEF · 2018
Leidenfrost Effect as a Reactor for Direct Methanol Fuel Cell Catalyst
Closest projects by meaning, across every fair and year in the corpus.
Source: Regeneron International Science and Engineering Fair